Huntsman Epoxy Adhesives

Home/Manufacturers/Huntsman/Huntsman Epoxy Adhesives
Huntsman Epoxy Adhesives 2017-08-18T18:54:45+00:00

 

Product designation Selected
specifications
Mixed
Viscosity
Work Life Curing Class Typ Service Temp. Lap Shear
Strength
T-Peel Characteristics
Conditions RT RT AI/AI
Unit (min) (min) (ºC) (ºC) (psi) (pli)
EPOXY ADHESIVES – Araldite
Araldite® 204 ABR2-0048 3 500 000 120 or 150
or 170
90 1 740/1 45 1-part foaming adhesive,
fills voids
(for core splicing),
extrudable paste
Item #5 ASNA 4125,
lss B/BMS 5-107
35 000-45 000
(semi-paste)
60-70 RT 82 3 500-5 100/580 22 Very high shear & peel strengths, bonds most metals, wood, rubber, composites, plastics
Item #5 ABR2-1079;
DAN 1284-01
45 000
(non-sag paste)
120 RT 60 3 625/1 160 28 (roller) Long open time,
high shear/peel strength,
dynamic load bearing,
electrically insulating, pumpable
Item #5 ABP 5-1158, iss 2 Thixotropic Paste 65 RT 60 3 000/700¹ 23(roller) Metallic appearance,gap-filling to 5mm good chemical & weather resistance,
bonds to metal, ceramic,
rubber & plastic
Item #5 ABP2-3094;
ABR2-0714
90 000 40 RT 120 2 400/2 400 17 (roller) High temperature,
chemical & water resistant,
gap-filling, bonds to wide
variety of substrates
Item #5 ABR2-1081 Thixotropic
(non-sag paste)
35 RT 80 3 500/1 050¹ 25(roller) Toughened, non-sag, gap-filling to 10mm, high shear & peel strength
Item #5 KIWA potable water;
FPI Europe
Non-flow paste 90 40-150 180 2 500/2 500 9-34 (roller) V high temperature & good
chemical resistance, gap-filling, bonds to wide range of substrates

0.50

Product designation Selected specifications Mixed Viscosity Work Life Curing Class Typ Service
Temp.
Lap Shear Strength T-Peel Characteristics
Conditions RT RT AI/AI
Unit (min) (min) (ºC) (ºC) (psi) (pli)
EPOXY ADHESIVES – Epibond
Epibond® 104 A/9831 AS 2149009-R;
BS 201-AA
Paste 3-4 RT 93 2 000-2 800/600-1 000² Quick-set to long work life with
3 hardeners (by increasing gel time), non-flow paste, gap-filling
Epibond® 104 A/946 20
Epibond® 104 A/104 B 30-40
Epibond® 156 A/B Motorola 11-14235
ACL
Soft paste 20-50 RT 121 2 000/1 950 RT Cure, low shrinkage, good electrical insulator, good for smoothing, filling (e.g. laminates, edges, radomes)
Epibond® 1210 A/B LAC 40-4093, CI B Semi-paste 50-75 RT 149 2 800/2 50 Low outgassing (spacecraft),
good high temperature properties
Epibond® 1210 A/9861 LAC 30-4639-0200 Semi-paste 35-60 RT 149 2 800/2 50 Low outgassing (spacecraft),
good high temperature properties
Epibond® 1217 A/B HMS 16-1068 CI 8B Paste4-8 RT 66 2 500/300 Fast set, translucent, 1:1 mix ratio
Epibond® 1534 A/B BMS 5-126, Ty 2, Cl 1 2 000 120 RT 82 3 000/575 Long work life, low viscosity,
high strength good fluid resistance
Epibond® 1539 A/B BMS 5-126, Ty 6, Cl 1 Paste 120 RT 82 2 500/800 Bonds to plastic, metal,
fiberglass reinforced composite
Epibond® 1544 products BMS 5-126, Ty IV,
Cl 1 or 4, Gr B
Semi-paste 10-20 RT 93 2 600/600 RT cure, early green strength, gap filling, flame retardant
Epibond® 1546 A/B Semi-paste 5-7 RT 60 3 000/- 9(T); 18(ro Very fast cure, good peel strength,
1:1 mix ratio
(w/w or v/v cartridge dispensed)
Epibond® 1559 products Airbus SIL 53-035,
App4; SS-8640
80 000 60 RT 70 2 900/3 00 Fast RT or low temp cure, flame retardant, 1:1 mix ratio
Epibond® 1565 A/B Boeing
D800-10411-1 PPD6-1
25 000
(non-sag paste)
720 177 150-177 1000/- Long work life, high temperature
performance, thixotropic paste
Araldite® 1570 A/B AIMS 10-04-006 220 000 60 RT 80 2 400/600 Polyolefin bonding, flame retardant (FAR 25.856)
Epibond® 1590 A/B AIMS 10-09-001 70 000 30 40-100 177 5 800/3 40 24-33 (roller) Roughened, low sag, 177°C performance
Epibond® 1590-3mm A/B AIMS 10-07-002 2 000 000 50 70 80 4 500/3 23 16.4 (roller) Gap-filling to 3mm, high strength,
good environmental stability
Epibond® 1590 FST A/B DANs 1199-01 &
1187-01
120 000 60 RT 120 3 200/1 60 22 (roller) Meets FAR 25.853 flame resistance criteria including smoke density & heat release, good hot/wet mechanical performance
Epocast® 1635 A/B BMS 5-28, Type 31
(QPL pending)
Semi-paste 60 RT 177 2 500-3 000?/ 2 500-3 Dynamic fatigue resistance for miss-drilled hole filling, high temperature lap shear & compressive strength
Epibond® 8543 C/B BMS 5-123, Ty 1, Cl3 Non-sag paste 3 7-RT 83 2 000/500 Very fast set, 1:1 mix ratio